A low-MFR block copolymer polypropylene combining rigidity with impact toughness for molded crates, buckets and durable containers.
Values below are typical and indicative only; final specifications are confirmed per lot and order.
| Melt Flow Rate (230C/2.16kg) | 1.0 - 3.0 g/10min |
|---|---|
| Density | 0.90 - 0.91 g/cm³ |
| Tensile Yield Stress | 21 - 26 MPa |
| Flexural Modulus | 900 - 1300 MPa (Typical ~1180) |
| Notched Izod Impact (23C) | 250 - 340 J/m |
| Notched Izod Impact (-20C) | 59 - 93 J/m |
| Vicat Softening Temp | ~ 150 °C |
| HDT (0.45 MPa) | 83 - 98 °C |
A single grade serving both extrusion compounding and thermoformed container production.
Pellets are melt-compounded and pelletized with controlled cooling to keep impact modifier well dispersed.
Sheet is heated and formed into crates, buckets and stackable containers with good wall strength.
Barrel 190-240°C; lower flow needs higher pressure and slightly longer fill.
20-60°C; warmer molds improve surface and impact on thick sections.
Adequate cooling avoids sink marks on ribbed crate and bucket geometries.
Stackable, impact-resistant crates for agriculture and logistics.
Chemical-resistant pails and buckets with rigid walls.
Storage and food containers with durable, reusable bodies.
Request a factory quote for Sinopec PP EPS30R in your required volume and packaging.